Singh, Chetan C.Chetan C.SinghPanda, EmilaEmilaPanda2025-08-302025-08-302018-05-0710.1063/1.49948942-s2.0-85046686656https://d8.irins.org/handle/IITG2025/22859A small variation in the elemental composition of a chemical compound can cause the formation of additional electronic defect states in the material, thereby altering the overall microstructure and thus induced properties. In this work, we observed chemical constitution-induced modification in the morphology and optoelectronic properties of SnS. To this end, SnS particles were prepared using the solution chemical route and were characterized using a wide range of experimental techniques, such as x-ray diffractometry, field emission scanning electron microscopy, high resolution transmission electron microscopy, energy dispersive spectroscopy (EDS), x-ray photoelectron spectroscopy (XPS), UV-Vis spectrophotometry, and scanning tunneling spectroscopy (STS). All these SnS particles are found to be Sn-rich and p-type. However, distinctly different morphologies (i.e., flower-like and aggregated ones) are observed. These are then correlated with the electronic defect states, which are induced because of the presence of Sn vacancies, Sn antisites, and/or Sn interstitials. A combination of EDS, XPS, and STS data confirmed the presence of a higher concentration of Sn vacancies along with lower quantities of Sn interstitials and/or antisites in the SnS particles with flower-like morphologies giving rise to higher hole concentration, which subsequently leads to reduced transport, optical band gaps, and barrier heights.falseArticle108975507 May 20185174904arJournal5WOS:000431651600028